Mechanism Of The Inhibition Afforded By Some Hydrazone Oxime Derivatives Towards Aluminium In 2m Naoh Solution
| المؤلف | Fouda, A. S. [عبد العزيز السيد فوده] |
| المؤلف | Elbaz, A. M. |
| المؤلف | Moussa, M. N. |
| تاريخ الإتاحة | 2009-11-25T15:31:50Z |
| تاريخ النشر | 1991 |
| اسم المنشور | Qatar University Science Journal |
| الاقتباس | Qatar University Science Journal, 1991, Vol. 11, Pages 95-11. |
| الملخص | The effect of some hydrazone oxime derivatives on the corrosion of aluminium in 2M NaOH solution was studied by polarization and weight-loss techniques. Polarization data indicated that all inhibitors tested were of a mixed type, and appeared to function through adsorption following the Temkin adsorption isotherm. The results showed that addition of Ba2* ions enhanced inhibition action by being chemisorbed on aluminium surface. The effect of temperature on the rate of corrosion with and without inhibitors was studied using weight-loss measurements. Some thermodynamic functions were also computed. |
| اللغة | en |
| الناشر | Qatar University |
| الموضوع | Chemistry الكيمياء |
| العنوان البديل | ميكانيكية منع تاكل الألومنيوم في محلول هيدروكسيد الصوديوم باستخدام بعض مشتقات هيدرازون - اكزيم |
| النوع | Article |
| الملخص البديل | استخدمت بعض مشتقات هيدرازون - اكزيم كموانع لتآكل الألومنيوم في محلول 2 ع هيدروكسيد الصوديوم وذلك باستخدام طريقة فقد الوزن وطريقة الاستقطاب . وقد دلت النتائج أيضا أن ميل هذه المركبات للادمصاص على الأسطح المعدنية تزد اد فى الاتجاه II < lv < vi < Ill < I وقد وجد أن اضافة ايونات الباريوم إلى الوسط تزيد من فعالية هذه المواد في منع التآكل وذلك بادمصاصها كيميائيا على سطح الألومنيوم . كلما درس أيخلا تأثير درجة الحرارة على معدل التآكل في وجود وفي عدم وجود هذه الموانع ، كما عينت ونوقشت بعض الدول اشيرموديناميكية لعملية الادمصاص . |