AbstractThe intrinsic viscosity, electrical conductivity and IR absorbance were measured for the sample of poly (4—ethylidene—1, 3—cyclopentylene vinylene). The sample is strongly oxidized in air. Under vacuum the activation energy is 1.38 eV at T > 377°K. The electrical conductivity of the annealed samples increases at low temperature and decreases at high temperature. The electrical conductivity of the samples which were exposed to air shows the metallic behaviour.
Languageen
PublisherQatar University
SubjectChemistry
الكيمياء
TitleThe electrical and optical properties of poly (4-ethylidene-l, 3-cyclopentylene vinylene)
Alternative Titleالتوصيل الكهربي والخواص البصرية للبولي ( 4 - إيثلدين - 1 ، 3 - سيكلوبنتلين فيلتايلين )
TypeArticle
Pagination95-101
Volume Number9
Alternative Abstractيعني هذا البحث يقاس التوصيل الكهربائي وكذلك دراسة الامتصاص بالأشعة تحت الحمراء واللزوجة الفعلية لعينة بولي ( 4 - إيثلدين - 1 ، 3 - سيكلوبنتيلين فينايلين ) وقد تم حساب قيمة طاقة التنشيط في غياب الهواء (under vacuum) وتساوي 1.38ev إلكترون فولت عند حوالي كلى 377k Tوقد وجد أن التوصيل الكهربي للعينات المستخدمة يزداد عند درجات حرارة منخفضة ويقل عند درجات حرارة مرتفعة . وقد وجد أن التوصيل الكهربي للعينات المعرضة للهواء توضح خاصية معدنية .
dc.accessType Open Access


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record