AbstractThe effect of surface parameters on corrosion behaviour of pure zinc in sodium sulphate solution was investigated. Surface parameters were determined using a Talysurf surface analyzer, and corrosion testing was performed using the Tafel plot technique. It was found that the corrosion rate decreases linearly with increasing the grit size while the polarization resistance increases. Also, it was found that the increase in surface roughness has two connecting effects. The first leads to a decrease in corrosion potential due to a decrease in the cathodic surface area while the second leads to an increase in corrosion potential due to a decrease in the peak to valley distances of surface irregularities
Languageen
PublisherQatar University
SubjectChemistry
الكيمياء
TitleInfluence Of Surface Finish Parameters On Corrosion Of Zinc
Alternative Titleتأثير تشطيب السطح على تآكل الزنك
TypeArticle
Alternative Abstractتم دراسة تأثير طريقة إعداد سطح العينة على تآكل الزنك النقي في محلول سلفات الصوديوم ، وقد لم قياس معاملات خشونة السطح بواسطة جهاز قياس خشونة الأسطح ( تيليسيرف ) وتم إجراء اختبارات التآكل باستخدام طريقة ( التافل ) . وقد وجد أن معدلات التآكل تتناسب تناسبا عكسيا مع زيادة حجم حبيبات التلميع للسطح بينما تقل مقاومة الاستقطاب . وقد أستنتج أن زياده خشونة السطح لها تأثيران متضادان ، أحدهما يؤدي إلى نقص في معدلات التآكل نتيجة نقص في المساحة الكاثودية بينما يؤدي الآخر إلى زيادة جهد التآكل نتيجة لنقص المسافات بين المرتفعات والمنخفضات غلى سطح العينات المتآكلة وقد تم التوصل إلى علاقات عددية تربط خشونة السطح مع معدلات التأكل للزنك .
dc.accessType Open Access


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record