The role of intermetallic compounds and composite-like structure development during dissimilar friction stir welding of aluminum to brass on metallurgical and flexural characteristics
| المؤلف | Esmaeili, A. |
| المؤلف | Hamouda, A. M. S. |
| تاريخ الإتاحة | 2021-07-05T11:03:42Z |
| تاريخ النشر | 2016 |
| اسم المنشور | Proceedings of 2016 7th International Conference on Mechanical and Aerospace Engineering, ICMAE 2016 |
| المصدر | Scopus |
| الملخص | In this study, the effects of developed Intermetallic Compounds (IMCs) and composite-like structure on metallurgical and flexural characteristics of the Friction Stir Welded (FSWed) joints were scrutinized and explored using OM, SEM equipped with EDS, and three-point bending test. Al2Cu was the main developed interfacial IMCs in the sound join; besides existence of a lamellar composite structure within the stir zone. The maximum bending angle was reached beyond 150 without any failure for optimum joint caused by proper mixing of materials. Thinness, continuity, and uniformity were the main observed characteristics of developed IMCs in the sound joint. 2016 IEEE. |
| اللغة | en |
| الناشر | Institute of Electrical and Electronics Engineers Inc. |
| الموضوع | Aluminum Brass Composite structure ductility flexural characteristic friction stir welding intermetallic compounds |
| النوع | Conference Paper |
| الصفحات | 64-67 |
الملفات في هذه التسجيلة
| الملفات | الحجم | الصيغة | العرض |
|---|---|---|---|
|
لا توجد ملفات لها صلة بهذه التسجيلة. |
|||
هذه التسجيلة تظهر في المجموعات التالية
-
الهندسة الميكانيكية والصناعية [1396 items ]