اسم المنشورJournal of Materials Engineering and Performance
المصدرScopus
الاقتباسAtieh, A.M., Khan, T.I. "Effect of Interlayer Thickness on Joint Formation Between Ti-6Al-4V and Mg-AZ31 Alloys" (2014) Journal of Materials Engineering and Performance, 23 (11), pp. 4042-4054.
الرقم المعياري الدولي للكتاب1059-9495
معرّف المصادر الموحدhttp://dx.doi.org/10.1007/s11665-014-1179-1
معرّف المصادر الموحدhttp://hdl.handle.net/10576/4530
الملخصThe joining of a Ti-6Al-4V alloy to a Mg-AZ31 alloy was performed using Ni electroplated coatings during the TLP bonding process. In this work, different coating thicknesses were used ranging from 1 to 20 μm. The effect of the coat thickness on microstructural developments and mechanical properties was studied. The bonded specimens were examined by metallographic examination, scanning electron microscopy, and X-ray diffraction analysis. It was observed that as the coat thickness increased from 1 to 12 μm, the joint shear strength increased from 9 to 47 MPa. A further increase in coat thickness had a detrimental effect on the bond strength, and a lower value of 11 MPa was recorded. The mechanism of joint formation includes three stages: solid-state diffusion, eutectic formation, and isothermal solidification.
راعي المشروعThe German Jordanian University (GJU), and NSERC Canada
اللغةen
الناشرSpringer New York LLC
الموضوعdiffusion
Mg-AZ31 alloy
microstructure
Ti-6Al-4V alloy
transient liquid phase (TLP) bonding
العنوانEffect of Interlayer Thickness on Joint Formation Between Ti-6Al-4V and Mg-AZ31 Alloys
النوعArticle
الصفحات4042-4054
رقم العدد11
رقم المجلد23
dc.accessType Abstract Only