المؤلفKhaled, M. M.
المؤلفYilbas, B. S.
المؤلفAl-Qaradawi, I. Y.
المؤلفColeman, P. G.
المؤلفAbdulmalik, D.
المؤلفSeddigi, Z. S.
المؤلفAbulkibash, A.
المؤلفAbu-Sharkh, B. F.
المؤلفEmad, M. M.
تاريخ الإتاحة2023-11-19T07:24:16Z
تاريخ النشر2006-10-05
اسم المنشورSurface and Coatings Technology
المعرّفhttp://dx.doi.org/10.1016/j.surfcoat.2006.01.019
الاقتباسKhaled, M. M., Yilbas, B. S., Al-Qaradawi, I. Y., Coleman, P. G., Abdulmalik, D., Seddigi, Z. S., ... & Emad, M. M. (2006). Corrosion properties of duplex treated Ti–6Al–4V alloy in chloride media using electrochemical and positron annihilation spectroscopy techniques. Surface and Coatings Technology, 201(3-4), 932-937.‏
الرقم المعياري الدولي للكتاب02578972
معرّف المصادر الموحدhttps://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=33748425104&origin=inward
معرّف المصادر الموحدhttp://hdl.handle.net/10576/49472
الملخصThe corrosion properties of duplex-treated and nitrided Ti-6Al-4V have been investigated in 0.025, 0.25 and 2.5 M NaCl using electrochemical techniques, Positron Annihilation Spectroscopy (PAS), X-ray diffraction (XRD), Scanning Electron Microscopy (SEM) and Energy Dispersive Spectrometry (EDS). The electrochemical results showed a three-fold increase in corrosion rate for every ten-fold increase in chloride concentration. The morphology and surface composition studied by XRD showed the presence of TiN and Ti2N layers. SEM and EDS showed the presence of pitting and the presence of oxide and chloride products. At the lowest concentration of NaCl no aluminum was detected in the surface layers while at the highest concentration no chloride byproducts were detected. PAS indicated that the damage caused by the NaCl changes in nature and becomes shallower as the concentration increases. © 2006 Elsevier B.V. All rights reserved.
اللغةen
الناشرElsevier B.V.
الموضوعCoating
Corrosion
Duplex
Laser
Ti-6Al-4V
TiN
العنوانCorrosion properties of duplex treated Ti-6Al-4V alloy in chloride media using electrochemical and positron annihilation spectroscopy techniques
النوعArticle
الصفحات932-937
رقم العدد3-4
رقم المجلد201
dc.accessType Abstract Only


الملفات في هذه التسجيلة

الملفاتالحجمالصيغةالعرض

لا توجد ملفات لها صلة بهذه التسجيلة.

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة