عرض بسيط للتسجيلة

المؤلفWaware, Umesh S.
المؤلفRashid, Mohd
المؤلفRahim, Afidah A.
المؤلفUmare, S. S.
تاريخ الإتاحة2024-03-11T06:39:25Z
تاريخ النشر2014-09-20
اسم المنشورBulletin of Materials Science
المعرّفhttp://dx.doi.org/10.1007/s12034-014-0053-y
الاقتباسWaware, U. S., Rashid, M., Rahim, A. A., & Umare, S. S. (2014). Synthesis and characterization of electroactive novel poly-2-cynoaniline. Bulletin of Materials Science, 37, 1131-1136.
الرقم المعياري الدولي للكتاب0250-4707
معرّف المصادر الموحدhttps://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84940280439&origin=inward
معرّف المصادر الموحدhttp://hdl.handle.net/10576/52858
الملخصUniform needle-like structures of poly-2-cynoaniline are formed without the use of any template by electrochemical oxidative polymerization method on copper electrode in acidic medium. The structural characterizations are performed by FT-IR, UV-Visible spectroscopy and X-ray diffraction studies. The morphology of the polymer is demonstrated by scanning electron microscopy (SEM). The framework of the needle-like structure, which is seen at low and high magnifications appeared as nanorods of 50–80 nm diameter and of length up to a few micrometres to form a scaffold of interconnected nanorods. Thermogravimetic analysis (TGA) indicates that poly-2-cynoaniline is thermally more stable than polyaniline. The conductivity of pressed pellet of the as-synthesized polymer measured at room temperature of 25 °C by four-probe measurement method was found to be 9.1824 × 10−5 S/cm. The polymer is easily dispersed in some organic solvents and shows high solubility.
راعي المشروعThis work was funded by Qatar University.
اللغةen
الناشرIndian Academy of Sciences
الموضوعConducting polymer
Nanorods
Poly-2-cynoaniline
العنوانSynthesis and characterization of electroactive novel poly-2-cynoaniline
النوعArticle
الصفحات1131-1136
رقم العدد5
رقم المجلد37
ESSN0973-7669
dc.accessType Full Text