الملخصThe effect of •y -irradiation on the thermodynamic parameters of LiKSC>4 single crystals, in the high temperature range 300-1000 K, is investigated. The results show that T,; as well as Cp decrease with dose rate. However, when the dose is greater than 10 MRad, both Cp and T,; increase with increasing dose. The analysis indicators that for high dose the interaction of defects is prominent, causing the stabilization of the low temperature phase. The energy of ferroelastic ordering (U), as well as the number of displaced atoms (N), were also estimated. It was found that, with increasing dose rate, U decreases while N increases
اللغةen
الناشرQatar University
الموضوعPhysics
الفيزياء
العنوانy - Irradiation Effect On The Ferroelastic High Temperature Phase In LiKSO4 Crystals
العنوان البديلتأثير إشعاعات جاما على التحول الطوري الفرومرن لبللورات من كبريتات الليثوم والبوتاسيوم
النوعArticle
الصفحات17-20
رقم المجلد12
الملخص البديلتم دراسة تأثير جرعات ومعدل الجرعات من أشعة جاما على بارامترات الديناميكا الحرارية للبلورات احادية من كبريتات الليثوم والبوتاسيوم في مدى حراري 300-1000 درجة مطلقة ، وقد أظهرت النتائج أن درجة حرارة التحويل الطوري Tc وكذلك الحرارة النوعية تحت ضغط ثابت Cp تقل بزيادة جرعات الاشعاع . وعند جرعات إشعاعية أكثر من 10 ميجاراد يكون Tc. Cf في زيادة مع الجرعة الاشعاعية . وبتحليل النتائج وجد أن التصادمات بين الشوائب يكون السائد ويسبب ثبات الطور المنخفض . كذلك حسبت كل من طاقة الترتيب الفرومون U وكذلك عدد الذرات المزاحة N ووجد أن طاقة الترتيب تزد اد مع زيادة معدل الجرعة الاشعاعية بينما يقل عدد الذرات المزاحة.