| الملخص | The E.P.R. linewidth of the M= + 1/2 <-» -1/2 transition of Fe3+ spectrum of Fe/MgO single crystals and powders have been measured at 9 GHz before and after annealing. The nominal iron concentrations ranged from 310 to 11900 p.p.m. Specimens were annealed at 500°C up to 24 hours. For single crystal, anneal¬ing produced reductions in peak-to-peak linewidth (AHpp) which occurred in two stages for all the spec¬imens examined. The values of the first and second decay rates were found to be concentration dependent. For powdered single crystal, annealing produced an increase in the peak-to-peak linewidth (AHpp). |
| اللغة | en |
| الناشر | Qatar University |
| الموضوع | Physics
|
| العنوان | Strain Broadening of E.P.R. Linewidths in Fe/Mgo Single Crystals and Powders |
| العنوان البديل | تأثير عرض الرنين المغناطيسي في مادة الحديد مع أوكسيد المغزيوم في حالة البلورة وحالة المسحوق |
| النوع | Article |
| الصفحات | 69-78 |
| رقم المجلد | 24 |
| الملخص البديل | تم قياس الرنين المغناطيس لمنتصف المقطع الانتقالي لطيف الحديد + 3 في مادة الحديد مع أوكسيد المغنيزيوم على هيئة بلورة وهيئة مسحوق عند تردد 9 جيجا هيلاتز قبل وبعد التسخين، أظهر التسخين عند درجة حرارة 500 مئوية خلال يوم كامل للتراكيز المختلفة التي تتراوح بين 130 – 11900 (وجزء من المليون) أن عرض خط طيف الرنين المغناطيسي يتغير تبعا لتغيير التركيز تغيرا واضحا في حالة البلورة بينما يتغير تغيرا خفيفا في حالة المسحوق. |