الملخصIn this paper, ZnSTe quantum dots-based hybrid solar cells (HSC) with two different device architectures have been investigated. The improved performance of the poly(3-hexylthiophene) (P3HT) and [6,6]phenyl C71 butyric acid methyl ester (PC71BM)-based bulk heterojunction (BHJ) solar cells by the incorporation of ZnSTe quantum dots (QDs) with an average size of 2.96 nm in PEDOT:PSS layer and active layer that have been demonstrated. Although the efficiency of both types of devices is almost the same, a close comparison reveals different reasons behind their improved performance. The device prepared with QDs in the HTL has shown reduced series resistance, increased shunt resistance, and improved mobility. On the other hand, QDs in the photoactive layer demonstrates increased photo-generation leading to improved efficiency.
اللغةen
الناشرSpringer Netherlands
الموضوعEnergy conversion
Hole transport layer
Mobility
Organic solar cell
Quantum dots
Rectification ratio
العنوانA comparative study on the performance of hybrid solar cells containing ZnSTe QDs in hole transporting layer and photoactive layer
النوعArticle
رقم العدد12
رقم المجلد18
dc.accessType Abstract Only


الملفات في هذه التسجيلة

الملفاتالحجمالصيغةالعرض

لا توجد ملفات لها صلة بهذه التسجيلة.

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة