الملخصCobalt oxides nanopowders were prepared using novel cellulose assisted combustion synthesis and solution combustion synthesis techniques. The synthesis conditions were optimized to produce high surface area cobalt oxide nanopowders. Effect of precursors ratio on product properties (such as crystalline structure, nanoparticle size, surface area etc.) were studied and compared for the two methods. Thermodynamic calculations along with TGA/DTA studies were used to understand the synthesis mechanism leading to cobalt oxide formation. The synthesized nanopowders were characterized using various materials characterization techniques such as XRD, SEM and TEM.
راعي المشروعQatar Foundation;Qatar National Research Fund
اللغةen
الناشرElsevier Ltd
الموضوعCellulose assisted combustion synthesis
Cobalt oxide nanopowder
Impregnated layer combustion synthesis
Solution combustion synthesis
العنوانCobalt oxide nanopowder synthesis using cellulose assisted combustion technique
النوعArticle
الصفحات12771-12777
رقم العدد11
رقم المجلد42
dc.accessType Abstract Only


الملفات في هذه التسجيلة

الملفاتالحجمالصيغةالعرض

لا توجد ملفات لها صلة بهذه التسجيلة.

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة