المؤلفAlbedah, M.A.
المؤلفAl-Qadi, K.
المؤلفStadnik, Z.M.
المؤلفPrzewoznik, J.
تاريخ الإتاحة2016-01-14T13:24:27Z
تاريخ النشر2014-11
اسم المنشورJournal of Alloys and Compounds
المصدرScopus
المعرّفhttp://dx.doi.org/10.1016/j.jallcom.2014.05.115
الاقتباسAlbedah, M.A., Al-Qadi, K., Stadnik, Z.M., Przewoznik, J., "Antiferromagnetism in EuPdGe3", (2014) Journal of Alloys and Compounds, 613, pp. 344-350
الرقم المعياري الدولي للكتاب0925-8388
معرّف المصادر الموحدhttp://hdl.handle.net/10576/4095
الملخصThe results of X-ray diffraction, magnetic susceptibility and magnetization, and 151Eu Mössbauer spectroscopy measurements of polycrystalline EuPdGe3 are reported. EuPdGe3 crystallizes in the BaNiSn3-type tetragonal structure (space group I4mm) with the lattice constants a=4.4457(1)Å and c=10.1703(2)Å. The results are consistent with EuPdGe3 being an antiferromagnet with the Néel temperature TN=12.16(1)K and with the Eu spins S=7/2 in the ab plane. The temperature dependence of the magnetic susceptibility above TN follows the modified Curie-Weiss law with the effective magnetic moment of 7.82(1) μB per Eu atom and the paramagnetic Curie temperature of -5.3(1)K indicative of dominant antiferromagnetic interactions. The M(H) isotherms for temperatures approaching TN from above are indicative of dynamical short-range antiferromagnetic ordering in the sample. The temperature dependence of the hyperfine magnetic field follows a S=7/2 Brillouin function. The principal component of the electric field gradient tensor is shown to increase with decreasing temperature and is well described by a T3/2 power-law relation. The Debye temperature of EuPdGe3 determined from the Mössbauer data is 199(2)K.
راعي المشروعNatural Sciences and Engineering Research Council of Canada.
اللغةen
الناشرElsevier Ltd
الموضوعAntiferromagnet
العنوانAntiferromagnetism in EuPdGe3
النوعArticle
الصفحات344-350
رقم المجلد613