Thermally conductive polyethylene/expanded graphite composites as heat transfer surface: Mechanical, thermo-physical and surface behavior
![Thumbnail](/xmlui/bitstream/handle/10576/44822/polymers-12-02863.pdf.jpg?sequence=3&isAllowed=y)
View/ Open
Date
2020Author
Sobolčiak, PatrikAbdulgader, Asma
Mrlik, Miroslav
Popelka, Anton
A. Abdala, Ahmed
A. Aboukhlewa, Abdelnasser
Karkri, Mustapha
Kiepfer, Hendrik
Bart, Hans-Jörg
Krupa, Igor
...show more authors ...show less authors
Metadata
Show full item recordAbstract
Composites of high-density polyethylene (HDPE) and expanded graphite (EG) are prepared for heat exchangers in multi-effect distillation (MED) desalination. At 50 wt.% EG loading, the thermal conductivity of HDPE was increased by 372%. Moreover, the surface wettability of the HDPE/EG composite was enhanced by corona and RF plasma treatment as demonstrated by the increase in surface free energy from 28.5 mJ/m2 for untreated HDPE/EG to 55.5 and 54.5 mJ/m2 for HDPE/EG treated by corona and RF plasma, respectively. This enhanced surface wettability was retained over a long time with only a 9% and 18% decrease in RF and corona plasma-treated samples' surface energy after two months. The viscoelastic moduli and the complex viscosity profiles indicated that EG content dictates the optimum processing technique. At loading below 30 wt.%, the extrusion process is preferred, while above 30 wt.% loading, injection molding is preferred. The plasma treatment also improved the HDPE/EG composite overall heat transfer coefficient with an overall heat transfer coefficient of the composite reaching about 98% that of stainless steel. Moreover, the plasma-treated composite exhibited superior resistance to crystallization fouling in both CaSO4 solution and artificial seawater compared to untreated composites and stainless-steel surfaces.