Effect of Interlayer Thickness on Joint Formation Between Ti-6Al-4V and Mg-AZ31 Alloys
المؤلف | Atieh, Anas M. |
المؤلف | Khan, Tahir I. |
تاريخ الإتاحة | 2016-05-16T10:55:24Z |
تاريخ النشر | 2014-11 |
اسم المنشور | Journal of Materials Engineering and Performance |
المصدر | Scopus |
الاقتباس | Atieh, A.M., Khan, T.I. "Effect of Interlayer Thickness on Joint Formation Between Ti-6Al-4V and Mg-AZ31 Alloys" (2014) Journal of Materials Engineering and Performance, 23 (11), pp. 4042-4054. |
الرقم المعياري الدولي للكتاب | 1059-9495 |
الملخص | The joining of a Ti-6Al-4V alloy to a Mg-AZ31 alloy was performed using Ni electroplated coatings during the TLP bonding process. In this work, different coating thicknesses were used ranging from 1 to 20 μm. The effect of the coat thickness on microstructural developments and mechanical properties was studied. The bonded specimens were examined by metallographic examination, scanning electron microscopy, and X-ray diffraction analysis. It was observed that as the coat thickness increased from 1 to 12 μm, the joint shear strength increased from 9 to 47 MPa. A further increase in coat thickness had a detrimental effect on the bond strength, and a lower value of 11 MPa was recorded. The mechanism of joint formation includes three stages: solid-state diffusion, eutectic formation, and isothermal solidification. |
راعي المشروع | The German Jordanian University (GJU), and NSERC Canada |
اللغة | en |
الناشر | Springer New York LLC |
الموضوع | diffusion Mg-AZ31 alloy microstructure Ti-6Al-4V alloy transient liquid phase (TLP) bonding |
النوع | Article |
الصفحات | 4042-4054 |
رقم العدد | 11 |
رقم المجلد | 23 |