المؤلفFayyad, Eman M.
المؤلفSadasivuni, Kishor Kumar
المؤلفPonnamma, Deepalekshmi
المؤلفAl-Maadeed, Mariam Al Ali
تاريخ الإتاحة2016-09-21T08:13:33Z
تاريخ النشر2016-10
اسم المنشورCarbohydrate Polymers
المصدرScopus
المعرّفhttp://dx.doi.org/10.1016/j.carbpol.2016.06.001
الاقتباسFayyad, E.M., Sadasivuni, K.K., Ponnamma, D., Al-Maadeed, M.A.A. "Oleic acid-grafted chitosan/graphene oxide composite coating for corrosion protection of carbon steel" (2016) Carbohydrate Polymers, 151, pp. 871-878.
الرقم المعياري الدولي للكتاب0144-8617
معرّف المصادر الموحدhttp://hdl.handle.net/10576/4749
الملخصAn anticorrosion coating film based on the formation of nanocomposite coating is reported in this study. The composite consisted of chitosan (green matrix), oleic acid, and graphene oxide (nano filler). The nanocomposite coating was arranged on the surface of carbon steel, and the corrosion resistance was monitored using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PP). Compared to the pure chitosan (CS) coating, the corrosion resistance of oleic acid-modified chitosan/graphene oxide film (CS/GO-OA) is increased by 100 folds. Since the well-dispersed smart grafted nanolayers delayed the penetration rate of corrosive species and thus maintained long term anticorrosive stability which is correlated with hydrophobicity and permeability.
راعي المشروعNPRP grant 4-800-2-297 from the Qatar National Research Fund (a member of Qatar Foundation).
اللغةen
الناشرElsevier Ltd
الموضوعCorrosion
Permeability
Hydrophobicity
Coating
Grafting
Chitosan
العنوانOleic acid-grafted chitosan/graphene oxide composite coating for corrosion protection of carbon steel
النوعArticle
الصفحات871-878
رقم المجلد151
dc.accessType Abstract Only