Show simple item record

AuthorAbbas, M. K.G.
AuthorAbdella, Galal M.
AuthorEltai, E. O.
Available date2024-02-22T06:51:29Z
Publication Date2020-01-01
Publication NameMaterials Today: Proceedings
Identifierhttp://dx.doi.org/10.1016/j.matpr.2020.07.252
CitationAbbas, M. K. G., Abdella, G. M., & Eltai, E. O. (2021). The impact of the corrosive environment on the quality of metal joining process. Materials Today: Proceedings, 46, 1613-1617.‏
URIhttps://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=85112514940&origin=inward
URIhttp://hdl.handle.net/10576/52079
AbstractOwing to the main attention as regards the metal joining in the automotive industries, many studies have been conducted to achieve this problem by joining metals materials that can provide high efficiency at minimum cost. However, one of the main factors to be considered is the metal corrosion when exposed to a corrosive environment. Consequently, this paper examines the effect of corrosion on the degradation of mechanical properties on the metal sheets joined by the seaming technique. The effect of corrosion on the joining strength was examined by immersing specimens in nitric acid solution. The tensile experiment was conducted under three different conditions. As supplied specimens, specimens were corroded before the joining process, and specimens were corroded after the joining process. The results showed that deterioration of corrosion affects the efficiency of the joints, causing early failure of the mechanical joint on specimens that were joined before exposure to a corrosive environment. Furthermore, it was observed that the effect of corrosion degradation on the sheet metal that corroded before the assembly process has excellent durability properties compared to the sheet metal, which exposed to the corrosive environment after assembly.
SponsorThis paper was made possible by internal grant No. QUSD-CENG-2018\2019-5 from Qatar University fund. The statements made herein are solely the responsibility of the authors.
Languageen
PublisherElsevier Ltd
SubjectCarbon Steel
Corrosion
Experimentation
Plastic deformation
Sheet metals
TitleThe impact of the corrosive environment on the quality of metal joining process
TypeConference Paper
Pagination1613-1617
Volume Number46
dc.accessType Abstract Only


Files in this item

FilesSizeFormatView

There are no files associated with this item.

This item appears in the following Collection(s)

Show simple item record