Synthesis and characterization of electroactive novel poly-2-cynoaniline
المؤلف | Waware, Umesh S. |
المؤلف | Rashid, Mohd |
المؤلف | Rahim, Afidah A. |
المؤلف | Umare, S. S. |
تاريخ الإتاحة | 2024-03-11T06:39:25Z |
تاريخ النشر | 2014-09-20 |
اسم المنشور | Bulletin of Materials Science |
المعرّف | http://dx.doi.org/10.1007/s12034-014-0053-y |
الاقتباس | Waware, U. S., Rashid, M., Rahim, A. A., & Umare, S. S. (2014). Synthesis and characterization of electroactive novel poly-2-cynoaniline. Bulletin of Materials Science, 37, 1131-1136. |
الرقم المعياري الدولي للكتاب | 0250-4707 |
الملخص | Uniform needle-like structures of poly-2-cynoaniline are formed without the use of any template by electrochemical oxidative polymerization method on copper electrode in acidic medium. The structural characterizations are performed by FT-IR, UV-Visible spectroscopy and X-ray diffraction studies. The morphology of the polymer is demonstrated by scanning electron microscopy (SEM). The framework of the needle-like structure, which is seen at low and high magnifications appeared as nanorods of 50–80 nm diameter and of length up to a few micrometres to form a scaffold of interconnected nanorods. Thermogravimetic analysis (TGA) indicates that poly-2-cynoaniline is thermally more stable than polyaniline. The conductivity of pressed pellet of the as-synthesized polymer measured at room temperature of 25 °C by four-probe measurement method was found to be 9.1824 × 10−5 S/cm. The polymer is easily dispersed in some organic solvents and shows high solubility. |
راعي المشروع | This work was funded by Qatar University. |
اللغة | en |
الناشر | Indian Academy of Sciences |
الموضوع | Conducting polymer Nanorods Poly-2-cynoaniline |
النوع | Article |
الصفحات | 1131-1136 |
رقم العدد | 5 |
رقم المجلد | 37 |
ESSN | 0973-7669 |
الملفات في هذه التسجيلة
هذه التسجيلة تظهر في المجموعات التالية
-
الهندسة الميكانيكية والصناعية [1341 items ]