المؤلفIsmail, Raid A. [رائد عبدالوهاب إِسماعيل]
المؤلفMoussa, Ali M.
تاريخ الإتاحة2009-11-25T15:12:07Z
تاريخ النشر1996
اسم المنشورQatar University Science Journal
الاقتباسQatar University Science Journal, 1996, Vol. 16, No. 2, Pages 245-249.
معرّف المصادر الموحدhttp://hdl.handle.net/10576/9636
الملخصIn this work the volume diffusion coefficients and profile distribution of Al impurities in molten germanium have been measured using secondary-iron mass spectroscopy (SIMS) technique. Diffusion is achieved with aid of Nd:Yag laser pulses. In this study it is shown that the diffusion coefficients and profile distribution of impurities are extremely sensitive to laser energy density. The calculated diffusion coefficients are ranging from 6.69 x 10"9 to 5.9 x 10~9 cm2.s'l
اللغةen
الناشرQatar University
الموضوعPhysics
الفيزياء
العنوانAnalysis Of Al Diffusion In Molten Germanium Induced By Pulsed Nd: Yag Laser Using Sims Technique
العنوان البديلدراسة تحليلية للانتشار المحتث بالليزر النبضي لشوائب الالومنيوم في منصهر الجرمانيوم باستخدام تقنية المطياف الكتلي للأيونات الثانوية
النوعArticle
الصفحات245-249
رقم العدد2
رقم المجلد16
الملخص البديلفي هذه الدراسة تم قياس معامل وشكل انتشار شوائب الألومنيوم في منصهر الجرمانيوم باستخدام تقنية المطياف الكتلي للأيونات الثانوية، حيث تم استخدام ليزر النديميوم - ياك النبضي في عملية الانتشار المحتث . من الحسابات ظهر اًن معامل الانتشار وهيئة توزيع شوائب الألومنيوم في الجرمانيوم تعتمد بشكل كبير على كثافة طاقة نبضة الليزر، وقد أوضحت النتائج أن مقدار معامل الانتشار تراوح ما بين 6.69*10-9 -8 و 5*10-8 سم2 / ث
dc.accessType Open Access


الملفات في هذه التسجيلة

Thumbnail

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة