الملخصThe effect of thermal and chemical treatments on the variation of specific surface area of porous bentonite as a support was studied. The surface area of bare bentonite thermally treated at 950°C and then washed with 6N HC1 was measured to be 3.01 m^/g. Chemical grafting for the same treated bentonite by the condensation of PEG-20 M at 280° C formed a non-extractable monomolecular layer of PEG-20M. This grafting process changed the surface structure of bare bentonite and contributed to the good separation of hydrocarbon mixture C5-C12 with a very good precision and sensitivity.
اللغةen
الناشرQatar University
الموضوعPhysical Chemistry
الكيمياء الفيزيائية
العنوانEffect of chemical grafting on the surface structure of porous bentonite as a support in gas chromatography
العنوان البديلتأثير التطعيم الكيميائي في البنية السطحية للبنتونيت المسامي كعامل في الكروماتوغرافيا
النوعArticle
الصفحات175-177
رقم العددخاص
رقم المجلد14
الملخص البديلفي هذا البحث تم دراسة تأثير تكرار المعالجة الكيميائية والحرارية على تغير المساحة السطحية النوعية للبنتونيت حيث وجد أن مساحة سطح البنتونيت المعالج عند 950ْ ثم بحمض ECL تبلغ 3.01 م2/جرا م. كما تم دراسة تأثير التطعيم الكيميائي للبنتونيت (المعالج حرارياً وكيميائياً ، وفقاً لما ذكر أعلاه ) بالبولي اثيلين جليكول M 20 (PEG – 20 M)على بنيته السطحية ، حيث أصبحت البنية السطحية له هي بنية البولي ايثيلين جليكول 20M وقد ساهم هذا مساهمة فعالة في التمكن من فصل مزائج الفحوم الهيدروجينية اللاقطبية من C5 إلى C12 بشكل أكثر دقة وحساسية من استخدام البنتونيت العاري أو المشروب بالبولي ايثيلين جليكول 20M .