الملخصThin films of cadmium stannate were prepared using thermal chemical spray pyrols: Cadmium stannate' solution (0.2M) was prepared by dissolution of CdCl25H2O in C2H5OH tion of SnCl23H2O in CH3COOH at molar 2:1, respectively. The Cd2Sn04 solution was spra substrate that was kept at 300°C. The studies of structure showed that the prepared thin film phous. After annealing, no changes observed in the films' structure. The type of electronic t determined by studying the Ultra Violet/Visible (UV/Vis) spectrum. Energy's gap, width of lo tail, refraction coefficient, reflection index, and extinction coefficient were calculated bef annealing. The optical constants were increased by increasing annealing's temperature and ness.
اللغةen
الناشرQatar University
الموضوعPhysics
العنوانThe Optical properties of Cadmium Stannate (Cd2SnO4) Thin Films Prepared by Chemical Spry Pyrolysis Technique
العنوان البديلدراسة الخواص البصرية لأغشية استينات الكادميوم (cd4 sno4) الرقيقة المحضرة بطريقة الرش الكيميائي الحراري
النوعArticle
الصفحات79-90
رقم المجلد24
الملخص البديلأغشية استينات الكادميوم لم (Cd4 SnO4) الرقيقة حضرت باستخدام تقنية الرش الكيميائي الحراري على قواعد زجاجية وبدرجة حرارة الغرفة وبأسماك مختلفة في حدود (3000A – 6000A) الخواص البصرية للأغشية العشوائية التركيب درست قبل وبعد التلدين ealing) حيث تم تعيين نوع الانتقالات الإلكترونية وحساب قيمه فجوة الطاقة البصرية ولوحظ إن قيمه فجوة الطاقة البصرية تقل مع زيادة سمك الأغشية وأن عرض ذيول الطاقة ومعامل الخمود ومعامل الانكسار ومعامل الانعكاس تتناسب طرديا مع زيادة درجه حرارة التلدين وسمك الأغشية المحضرة.
dc.accessType Open Access


الملفات في هذه التسجيلة

Thumbnail

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة