The electrical and optical properties of poly (4-ethylidene-l, 3-cyclopentylene vinylene)
| المؤلف | Shahada, Lamis [لميس شحادة] |
| المؤلف | El-Shekeil, Ali |
| المؤلف | Mounir, M. |
| تاريخ الإتاحة | 2009-11-25T15:24:57Z |
| تاريخ النشر | 1989 |
| اسم المنشور | Qatar University Science Bulletin |
| الاقتباس | Qatar University Science Bulletin, 1989, Vol. 9, Pages 95-101. |
| الملخص | The intrinsic viscosity, electrical conductivity and IR absorbance were measured for the sample of poly (4—ethylidene—1, 3—cyclopentylene vinylene). The sample is strongly oxidized in air. Under vacuum the activation energy is 1.38 eV at T > 377°K. The electrical conductivity of the annealed samples increases at low temperature and decreases at high temperature. The electrical conductivity of the samples which were exposed to air shows the metallic behaviour. |
| اللغة | en |
| الناشر | Qatar University |
| الموضوع | Chemistry الكيمياء |
| العنوان البديل | التوصيل الكهربي والخواص البصرية للبولي ( 4 - إيثلدين - 1 ، 3 - سيكلوبنتلين فيلتايلين ) |
| النوع | Article |
| الصفحات | 95-101 |
| رقم المجلد | 9 |
| الملخص البديل | يعني هذا البحث يقاس التوصيل الكهربائي وكذلك دراسة الامتصاص بالأشعة تحت الحمراء واللزوجة الفعلية لعينة بولي ( 4 - إيثلدين - 1 ، 3 - سيكلوبنتيلين فينايلين ) وقد تم حساب قيمة طاقة التنشيط في غياب الهواء (under vacuum) وتساوي 1.38ev إلكترون فولت عند حوالي كلى 377k Tوقد وجد أن التوصيل الكهربي للعينات المستخدمة يزداد عند درجات حرارة منخفضة ويقل عند درجات حرارة مرتفعة . وقد وجد أن التوصيل الكهربي للعينات المعرضة للهواء توضح خاصية معدنية . |