The electrical and optical properties of poly (4-ethylidene-l, 3-cyclopentylene vinylene)
| Author | Shahada, Lamis [لميس شحادة] |
| Author | El-Shekeil, Ali |
| Author | Mounir, M. |
| Available date | 2009-11-25T15:24:57Z |
| Publication Date | 1989 |
| Publication Name | Qatar University Science Bulletin |
| Citation | Qatar University Science Bulletin, 1989, Vol. 9, Pages 95-101. |
| Abstract | The intrinsic viscosity, electrical conductivity and IR absorbance were measured for the sample of poly (4—ethylidene—1, 3—cyclopentylene vinylene). The sample is strongly oxidized in air. Under vacuum the activation energy is 1.38 eV at T > 377°K. The electrical conductivity of the annealed samples increases at low temperature and decreases at high temperature. The electrical conductivity of the samples which were exposed to air shows the metallic behaviour. |
| Language | en |
| Publisher | Qatar University |
| Subject | Chemistry الكيمياء |
| Alternative Title | التوصيل الكهربي والخواص البصرية للبولي ( 4 - إيثلدين - 1 ، 3 - سيكلوبنتلين فيلتايلين ) |
| Type | Article |
| Pagination | 95-101 |
| Volume Number | 9 |
| Alternative Abstract | يعني هذا البحث يقاس التوصيل الكهربائي وكذلك دراسة الامتصاص بالأشعة تحت الحمراء واللزوجة الفعلية لعينة بولي ( 4 - إيثلدين - 1 ، 3 - سيكلوبنتيلين فينايلين ) وقد تم حساب قيمة طاقة التنشيط في غياب الهواء (under vacuum) وتساوي 1.38ev إلكترون فولت عند حوالي كلى 377k Tوقد وجد أن التوصيل الكهربي للعينات المستخدمة يزداد عند درجات حرارة منخفضة ويقل عند درجات حرارة مرتفعة . وقد وجد أن التوصيل الكهربي للعينات المعرضة للهواء توضح خاصية معدنية . |