AuthorFouda, A. S. [عبد العزيز السيد فوده]
AuthorElbaz, A. M.
AuthorMoussa, M. N.
Available date2009-11-25T15:31:50Z
Publication Date1991
Publication NameQatar University Science Journal
CitationQatar University Science Journal, 1991, Vol. 11, Pages 95-11.
URIhttp://hdl.handle.net/10576/10266
AbstractThe effect of some hydrazone oxime derivatives on the corrosion of aluminium in 2M NaOH solution was studied by polarization and weight-loss techniques. Polarization data indicated that all inhibitors tested were of a mixed type, and appeared to function through adsorption following the Temkin adsorption isotherm. The results showed that addition of Ba2* ions enhanced inhibition action by being chemisorbed on aluminium surface. The effect of temperature on the rate of corrosion with and without inhibitors was studied using weight-loss measurements. Some thermodynamic functions were also computed.
Languageen
PublisherQatar University
SubjectChemistry
الكيمياء
TitleMechanism Of The Inhibition Afforded By Some Hydrazone Oxime Derivatives Towards Aluminium In 2m Naoh Solution
Alternative Titleميكانيكية منع تاكل الألومنيوم في محلول هيدروكسيد الصوديوم باستخدام بعض مشتقات هيدرازون - اكزيم
TypeArticle
Alternative Abstractاستخدمت بعض مشتقات هيدرازون - اكزيم كموانع لتآكل الألومنيوم في محلول 2 ع هيدروكسيد الصوديوم وذلك باستخدام طريقة فقد الوزن وطريقة الاستقطاب . وقد دلت النتائج أيضا أن ميل هذه المركبات للادمصاص على الأسطح المعدنية تزد اد فى الاتجاه II < lv < vi < Ill < I وقد وجد أن اضافة ايونات الباريوم إلى الوسط تزيد من فعالية هذه المواد في منع التآكل وذلك بادمصاصها كيميائيا على سطح الألومنيوم . كلما درس أيخلا تأثير درجة الحرارة على معدل التآكل في وجود وفي عدم وجود هذه الموانع ، كما عينت ونوقشت بعض الدول اشيرموديناميكية لعملية الادمصاص .