الملخصThe E.P.R. linewidth of the M= + 1/2 <-» -1/2 transition of Fe3+ spectrum of Fe/MgO single crystals and powders have been measured at 9 GHz before and after annealing. The nominal iron concentrations ranged from 310 to 11900 p.p.m. Specimens were annealed at 500°C up to 24 hours. For single crystal, anneal¬ing produced reductions in peak-to-peak linewidth (AHpp) which occurred in two stages for all the spec¬imens examined. The values of the first and second decay rates were found to be concentration dependent. For powdered single crystal, annealing produced an increase in the peak-to-peak linewidth (AHpp).
اللغةen
الناشرQatar University
الموضوعPhysics
العنوانStrain Broadening of E.P.R. Linewidths in Fe/Mgo Single Crystals and Powders
العنوان البديلتأثير عرض الرنين المغناطيسي في مادة الحديد مع أوكسيد المغزيوم في حالة البلورة وحالة المسحوق
النوعArticle
الصفحات69-78
رقم المجلد24
الملخص البديلتم قياس الرنين المغناطيس لمنتصف المقطع الانتقالي لطيف الحديد + 3 في مادة الحديد مع أوكسيد المغنيزيوم على هيئة بلورة وهيئة مسحوق عند تردد 9 جيجا هيلاتز قبل وبعد التسخين، أظهر التسخين عند درجة حرارة 500 مئوية خلال يوم كامل للتراكيز المختلفة التي تتراوح بين 130 – 11900 (وجزء من المليون) أن عرض خط طيف الرنين المغناطيسي يتغير تبعا لتغيير التركيز تغيرا واضحا في حالة البلورة بينما يتغير تغيرا خفيفا في حالة المسحوق.