AbstractThe E.P.R. linewidth of the M= + 1/2 <-» -1/2 transition of Fe3+ spectrum of Fe/MgO single crystals and powders have been measured at 9 GHz before and after annealing. The nominal iron concentrations ranged from 310 to 11900 p.p.m. Specimens were annealed at 500°C up to 24 hours. For single crystal, anneal¬ing produced reductions in peak-to-peak linewidth (AHpp) which occurred in two stages for all the spec¬imens examined. The values of the first and second decay rates were found to be concentration dependent. For powdered single crystal, annealing produced an increase in the peak-to-peak linewidth (AHpp).
Languageen
PublisherQatar University
SubjectPhysics
TitleStrain Broadening of E.P.R. Linewidths in Fe/Mgo Single Crystals and Powders
Alternative Titleتأثير عرض الرنين المغناطيسي في مادة الحديد مع أوكسيد المغزيوم في حالة البلورة وحالة المسحوق
TypeArticle
Pagination69-78
Volume Number24
Alternative Abstractتم قياس الرنين المغناطيس لمنتصف المقطع الانتقالي لطيف الحديد + 3 في مادة الحديد مع أوكسيد المغنيزيوم على هيئة بلورة وهيئة مسحوق عند تردد 9 جيجا هيلاتز قبل وبعد التسخين، أظهر التسخين عند درجة حرارة 500 مئوية خلال يوم كامل للتراكيز المختلفة التي تتراوح بين 130 – 11900 (وجزء من المليون) أن عرض خط طيف الرنين المغناطيسي يتغير تبعا لتغيير التركيز تغيرا واضحا في حالة البلورة بينما يتغير تغيرا خفيفا في حالة المسحوق.
dc.accessType Open Access


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record