عرض بسيط للتسجيلة

المؤلفBensalah N.
المؤلفTurki D.
المؤلفKamand F.Z.
المؤلفSaoud K.
تاريخ الإتاحة2020-03-18T08:10:09Z
تاريخ النشر2018
اسم المنشورPhysica Status Solidi (A) Applications and Materials Science
المصدرScopus
الرقم المعياري الدولي للكتاب18626300
معرّف المصادر الموحدhttp://dx.doi.org/10.1002/pssa.201800151
معرّف المصادر الموحدhttp://hdl.handle.net/10576/13342
الملخصMulti-walled carbon nanotubes?manganese(II) fluoride (MWCNT?MnF2) composite was prepared by a simple two-step method. In the first step, a wet chemistry reaction between manganese (II) nitrate, Mn(NO3)2, and hexafluoroslicic acid, H2SiF6, produces manganese(II) hexafluorosilicate (MnSiF6). The thermal decomposition of MnSiF6 in presence of MWCNTs at 400 ?C under argon atmosphere releases SiF4 gas and forms MWCNT?MnF2 composite. Powder X-ray diffraction, Raman spectroscopy, and scanning electron microscopy confirmed the formation of pure phases of MnF2 nanoparticles with rutile crystalline structure with no impurity phases. MnF2 nanoparticles were dispersed among MWCNTs networks and partially decorating MWCNTs forming a hierarchically nanostructured MWCNT?MnF2 composite. Cyclic voltammetry (CV) and electrochemical impedance spectroscopy tests showed that the MWCNT?MnF2 composite electrode underwent electrochemical lithiation/delithiation reactions with enhanced reversibility and stabilized solid?electrolyte interface (SEI) during cycling. Charge?discharge tests demonstrated that the MWCNT?MnF2 electrode displayed an irreversible specific capacity in the first cycle mainly linked to the decomposition of the electrolyte and the formation of the SEI film. After 100 cycles, a charge specific capacity of 480 mAh g?1 MnF2 was measured (80% of the initial capacity) with high coulombic efficiency (CE) (?100%), indicating the high reversibility of electrochemical conversion reactions. X-ray photoelectron spectroscopy, XRD, and SEM-EDX analyses for non-cycled and fully discharged MWCNT?MnF2 electrodes confirmed the irreversible lithiation of MnF2 into Mn and LiF during the ten first charge?discharge cycles. The higher electrochemical performance of the composite electrode compared to pure MnF2 can be attributed to the hierarchical structure of MWCNT?MnF2, which is capable to assimilate the volume changes, stabilize the solid?electrolyte interface (SEI), and facilitate Li+ ions and electrons transfer. ? 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
راعي المشروعThis work was funded by a grant from the Qatar National Research Fund under its National Priorities Research Program award number NPRP7-567-2-216. Its contents are solely the responsibility of the authors and do not necessarily represent the official views of the Qatar National Research Fund.
اللغةen
الناشرWiley-VCH Verlag
الموضوعcomposite electrodes
electrochemical performance
Li ion batteries
manganese(II) fluoride
multi-walled carbon nanotubes
العنوانHierarchical Nanostructured MWCNT MnF2 Composites With Stable Electrochemical Properties as Cathode Material for Lithium Ion Batteries
النوعArticle
رقم العدد14
رقم المجلد215
dc.accessType Abstract Only


الملفات في هذه التسجيلة

الملفاتالحجمالصيغةالعرض

لا توجد ملفات لها صلة بهذه التسجيلة.

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة