الملخصIn this report, interlinked chitosan-ZnO nanocomposite at 10% ZnO (CZNC-10) is successfully used as green biocide for biofilm control and reduction of biocorrosion on carbon steel material. It was found that 250 g/mL CZNC-10 can be used efficiently for the inhibition of sulfate reducing bacteria (SRB) biofilm on carbon steel. The Rct values after 21 and 28 days of incubation in presence of CZNC-10 are almost 3.2 and 2.8 times higher than the control respectively, indicating a strong corrosion inhibition with 74% as maximum inhibition efficiency.
راعي المشروعThe authors acknowledge the financial support of Qatar National Research Fund (A member of Qatar Foundation) through the NPRP grants # NPRP8-286-2-118 . The authors are thankful to Maersk Oil Research and Technology Centre (MORTC), Doha, Qatar for providing the sludge samples and technical support. The authors are thankful to V Madhavan at the Core lab of QEERI/HBKU, Qatar for XPS analysis. Appendix A
اللغةen
الناشرElsevier Ltd
الموضوعBiofilm
Chitosan-ZnO
Electrochemical impedance spectroscopy
Microbial corrosion
SRB
العنوانControlling the biocorrosion of sulfate-reducing bacteria (SRB) on carbon steel using ZnO/chitosan nanocomposite as an eco-friendly biocide
النوعArticle
الصفحات397-406
رقم المجلد148
dc.accessType Abstract Only


الملفات في هذه التسجيلة

الملفاتالحجمالصيغةالعرض

لا توجد ملفات لها صلة بهذه التسجيلة.

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة