الملخصCopper ferrite (CuFe2O4) nanoparticles were prepared by the sol-gel auto-combustion method and used to construct a conductometric gas sensor in this work. The as-prepared CuFe2O4 nanoparticles were annealed at 500 °C and 750 °C. X-ray diffraction measurements as well as transmission electron microscopy were used to identify the crystal structure of as-prepared and annealed nanoparticles. The results reveal growth of nanoparticle size crystal structure as well as phase transition from cubic structure to tetragonal symmetry upon annealing. Fourier Transform Infra-Red Spectroscopy (FTIR) measurements of the CuFe2O4 nanoparticles revealed the tetrahedral and octahedral absorption bands that are characteristic of the spinel ferrite. Nanoparticle powder was pressed in a form of a pellet to form the gas sensor device. The pellet was placed between a copper sheet and a stainless steel grid for the bottom and top electrodes, respectively. The results revealed that the produced CuFe2O4 nanoparticles are sensitive to both H2S and H2, but with higher sensitivity to H2S at low temperatures. The gas sensitivity of the sensors could be investigated in terms of the large number of reactive surface sites due to the large surface area of the nanoparticles as well as the adsorption of oxygen species on the surface of nanoparticles.
راعي المشروعThis work was supported by the Petroleum Institute under a grant number RIFP-14312 and Qatar University under a grant number QUUG-CAS-DMSP-15?16-20.
اللغةen
الناشرElsevier Ltd
الموضوعCuFe2O4
Gas sensor
Hydrogen sulfide
Nanoparticles
Sol-gel
Spinal ferrite
العنوانCharacterization of H2S gas sensor based on CuFe2O4nanoparticles
النوعArticle
الصفحات461-468
رقم المجلد690
dc.accessType Abstract Only


الملفات في هذه التسجيلة

الملفاتالحجمالصيغةالعرض

لا توجد ملفات لها صلة بهذه التسجيلة.

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة