| الملخص | Abstract: Haematite (?-Fe2O3) nanoparticles (NPs) of different sizes and morphologies were prepared from two different iron precursors (iron acetate (A) and iron nitrate (N)) using the sol�gel technique, through a reaction with oxalic acid. A pure ?-Fe2O3 phase (rhombohedral) that contained particles of different sizes and shapes were obtained from both iron precursors. Transmission electron microscope measurements showed average sizes of 23 � 2 and 30 � 2 nm for ?-Fe2O3 (A) and ?-Fe2O3 (N) formed NPs, respectively. The observed uniform spherical shape for the ?-Fe2O3 (A) formed NPs is due to the presence of carboxylic acid (acetic acid) used to control the nucleation and growth process of ?-Fe2O3 NPs. However, quasi-spherical particle shapes for ?-Fe2O3 (N) were produced in the presence of a mineral acid (nitric acid), which caused the particles to be constrained during their growth step. However, the optical analysis showed that the band gaps of ?-Fe2O3 (A) and ?-Fe2O3 (N) as 2.63 and 2.60 eV were found, respectively. The surface area results exhibited that both ?-Fe2O3 NPs were a porous material with a higher area for ?-Fe2O3 (A), which resulted from the uniform shape and smaller size of particles. The magnetic properties were observed to be slightly different for both ?-Fe2O3 NPs, which were also attributed to the different particle size of the NPs. Higher photocatalytic activity for congo red dye and 4-chlorophenol degradation under sunlight was achieved by ?-Fe2O3 (A), which was attributed to the smaller size and higher surface area compared to ?-Fe2O3 (N) NPs. Graphical Abstract: [Figure not available: see fulltext.] |
| اللغة | en |
| الناشر | Springer New York LLC |
| الموضوع | Nanoparticles Photocatalytic activity Sol�gel Sunlight ?-Fe2O3 |
| النوع | Article |
| الصفحات | 880-893 |
| رقم العدد | 3 |
| رقم المجلد | 81 |
الملفات في هذه التسجيلة
| الملفات | الحجم | الصيغة | العرض |
|---|---|---|---|
|
لا توجد ملفات لها صلة بهذه التسجيلة. |
|||
هذه التسجيلة تظهر في المجموعات التالية
-
الأبحاث [499 items ]