Functionalization of silica-coated magnetic nanoparticles as powerful demulsifier to recover oil from oil-in-water emulsion
View/ Open
Publisher version (Check access options)
Check access options
Date
2021Metadata
Show full item recordAbstract
This study presents an innovative approach for the preparation of Fe3O4 nanoparticles covered with SiO2 shell (denoted as Fe–Si-MNP), which were used to recover oil recovery from oil-in-water emulsion (O/W-emul). The Fe–Si-MNP were prepared with differing silica layer thicknesses (5 nm [Fe–Si-1], 8 nm [Fe–Si-2], 10 nm [Fe–Si-3], and 15 nm [Fe–Si-4]) and tested for the percentage of oil separation (%Soil) under different dosages (DMNP), oil concentration (Doil), surfactant dosages (Dsur), and pH. The Fe–Si-MNP exhibited excellent %Soil, reliable stability, and high magnetization values ranging between 46.1 and 80.2 emu/g. adding a 5 nm silica layer on the surface of the Fe–Si-MNP (i.e., Fe–Si-1) protected them from oxidation conditions, extended their service life, and achieved a %Soil of ∼96.3%. The %Soil slightly decreased to ∼92% with an alkaline pH or when the thickness of the silica layer increased to ≥10 nm. The %Soil was 90.5%, 89.5%, and 87.5% for Fe–Si-2, Fe–Si-3, and Fe–Si-4, respectively. Increasing the water salinity from 0.1 to 0.5 M slightly improved the %Soil for the tests carried out with a Doil of 100 mg/L to 93.3%, 90.3%, and 86.3% for Fe–Si-2, Fe–Si-3, and FeSi-4, respectively. The highest %Soil achieved with Fe– Si-1 Fe–Si-2 and Fe–Si-3 was >95%, 95% and 92%, respectively. The Fe–Si-MNP exhibited a high recyclability for 9 cycles with the lowest %Soil ∼80%. The results suggest that the structure and properties of the Fe–Si-MNP can be manipulated to achieve a high oil recovery, easy separation, and extended service life.
Collections
- Chemical Engineering [1141 items ]