الملخصMembranes for direct contact membrane distillation were produced from electrospun polystyrene microfibers doped with activated carbon. The addition of activated carbon reduced the hydrophobicity of the fibers. Therefore, desalination membranes were fabricated in a multi-layer construction with undoped polystyrene as the outer layers and activated carbon-doped polystyrene as an inner layer. Membranes including activated carbon-doped layers showed a 20× greater specific surface area as compared to undoped membranes. The vapor flux of the membranes containing layers doped with activated carbon (6.3 ± 0.7 kg/m2/h) was not statistically different from that with an all polystyrene construction (8.1 ± 1.2 kg/m2/h). The membranes retained their desalination capabilities despite the addition of the activated carbon.
اللغةen
الناشرSpringer Nature
الموضوعActivated carbon
Electrospinning
Membrane distillation
Polystyrene
Volatile organic compounds
العنوانActivated carbon-doped polystyrene fibers for direct contact membrane desalination
النوعArticle
الصفحات807-814
رقم العدد6
رقم المجلد3
dc.accessType Abstract Only


الملفات في هذه التسجيلة

الملفاتالحجمالصيغةالعرض

لا توجد ملفات لها صلة بهذه التسجيلة.

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة