المؤلفGao P.
المؤلفHua X.
المؤلفDegirmenci V.
المؤلفRooney D.
المؤلفKhraisheh, Majeda
المؤلفPollard R.
المؤلفBowman R.M.
المؤلفRebrov E.V.
تاريخ الإتاحة2022-05-21T08:36:55Z
تاريخ النشر2013
اسم المنشورJournal of Magnetism and Magnetic Materials
المصدرScopus
المعرّفhttp://dx.doi.org/10.1016/j.jmmm.2013.07.060
معرّف المصادر الموحدhttp://hdl.handle.net/10576/31227
الملخصA series of nanostructured Ni-Zn ferrites Ni1-xZn xFe2O4 (x=0, 0.5 and 1) with a grain size from 24 to 65 nm have been prepared with a sol-gel method. The effect of composition and sintering temperature on morphology, magnetic properties, Curie temperature, specific heating rate at 295 kHz and hysteresis loss have been studied. The highest coercivity of 50 and 40 Oe, were obtained for NiFe2O 4 and Ni0.5Zn0.5Fe2O4 samples with the grain size of 35 and 29 nm, respectively. The coercivity of Ni and Ni-Zn mixed ferrites decreased with temperature. The Bloch exponent was 1.5 for all samples. As the grain size increased, the Curie temperature of NiFe 2O4 increased from 849 to 859 K. The highest saturation magnetization of 70 emu/g at 298 K and the highest specific heating rate of 1.6 K/s under radiofrequency heating at 295 kHz were observed over NiFe 2O4 calcined at 1073 K. Both the magnitude of the hysteresis loss and the temperature dependence of the loss are influenced by the sintering temperature and composition.
اللغةen
الموضوعFerrite
Magnetization
Radiofrequency heating
Sol-gel method
العنوانStructural and magnetic properties of Ni1-xZnxFe 2O4 (x=0, 0.5 and 1) nanopowders prepared by sol-gel method
النوعArticle
الصفحات44-50
رقم المجلد348
dc.accessType Abstract Only


الملفات في هذه التسجيلة

الملفاتالحجمالصيغةالعرض

لا توجد ملفات لها صلة بهذه التسجيلة.

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة