Poly (acrylonitrile-co-methyl methacrylate) nanoparticles: I. Preparation and characterization
![Thumbnail](/bitstream/handle/10576/31373/S1878535214002755.pdf.jpg?sequence=3&isAllowed=y)
عرض / فتح
اصدار الناشر (تحقق من خيارات الوصول)
تحقق من خيارات الوصول
التاريخ
2017البيانات الوصفية
عرض كامل للتسجيلةالملخص
This work concerns the preparation and characterization of poly (acrylonitrile-co-methyl methacrylate) Copolymer, P(AN-co-MMA), nano-particles using precipitation polymerization technique. Potassium per-sulfate redox initiation system was used to perform polymerization process in an alcoholic aqueous system. The impact of different polymerization conditions such as comonomer concentration and ratio, polymerization time, polymerization temperatures, initiator concentration and co-solvent composition on the polymerization yield and particle size was studied. Maximum polymerization yield, 70%, was obtained with MMA:AN (90%:10%) comonomer composition. Particle sizes ranging from 16 nm to 1483 nm were obtained and controlled by variation of polymerization conditions. The co-polymerization process was approved by FT-IR and TGA analysis. The copolymer composition was investigated by nitrogen content analysis. Copolymers with a progressive percentage of PAN show thermal stabilities close to PAN Homopolymer. SEM photographs prove spherical structure of the produced copolymers. The investigated system shows promising future in the preparation of nanoparticles from comonomers without using emulsifiers or dispersive agents.
المجموعات
- علم وتكنولوجيا المواد [293 items ]