Synthesis of silica supported ni and cu catalyst for carbon dioxide methanation reaction
المؤلف | Aheed, Ahmed |
المؤلف | Saleh Saad, Mohd Ali H. |
المؤلف | Kumar, Anand |
تاريخ الإتاحة | 2022-09-15T07:07:59Z |
تاريخ النشر | 2019 |
اسم المنشور | AIChE Annual Meeting, Conference Proceedings |
المصدر | Scopus |
الملخص | In this study we investigate the synthesis of nickel and copper catalyst supported on silica for CO2 conversion to methane. The activity and product selectivity and stability for methanation reaction on Ni/SiO2 and Cu/SiO2 catalysts have been evaluated using a flow reactor between 50ºC - 650ºC. The as-synthesized catalysts were characterized using XRD, SEM, TEM to understand the structural properties. In addition, the used catalysts after the reaction were characterized using similar techniques to evaluate the effect of reaction conditions on active phase and SiO2 support. The 1%Ni on SiO2 catalyst shows good activity for CO2 conversion to CH4 till 450ºC, thereafter CH4 formation decreased and CO increased and remains the only product at 650ºC. The Ni/SiO2 catalyst shows excellent stability without any deactivation till 2700 min of TOS at 650ºC. The other catalysts, 1%Cu on SiO2 was also promising however, it is exclusively selective to CO and no trace of CH4 was obtained. |
راعي المشروع | This publication was made possible by NPRP grant (NPRP8-509-2-209) from the Qatar national research fund (a member of Qatar foundation).The statements made herein are solely the responsibility of the author(s). The authors also wish to acknowledge the technical services granted by Central Laboratory Unit (CLU) and Gas Processing Centre (GPC) at Qatar University. |
اللغة | en |
الناشر | American Institute of Chemical Engineers |
الموضوع | Carbon dioxide conversion CO2 methanation Nickel SiO2 Solution combustion synthesis |
النوع | Conference Paper |
رقم المجلد | 2019-November |
الملفات في هذه التسجيلة
الملفات | الحجم | الصيغة | العرض |
---|---|---|---|
لا توجد ملفات لها صلة بهذه التسجيلة. |
هذه التسجيلة تظهر في المجموعات التالية
-
الهندسة الكيميائية [1141 items ]