عرض بسيط للتسجيلة

المؤلفBahgat Radwan, A.
المؤلفMannah, Cheirva A.
المؤلفSliem, Mostafa H.
المؤلفAl-Qahtani, Noora Hamad S.
المؤلفOkonkwo, Paul C.
المؤلفBerdimurodov, Elyor
المؤلفMohamed, Adel M.
المؤلفAbdullah, Aboubakr M.
تاريخ الإتاحة2022-09-25T05:51:36Z
تاريخ النشر2021-11-01
اسم المنشورJournal of Applied Electrochemistry
المعرّفhttp://dx.doi.org/10.1007/s10800-021-01603-8
الاقتباسBahgat Radwan, A., Mannah, C. A., Sliem, M. H., Al-Qahtani, N. H. S., Okonkwo, P. C., Berdimurodov, E., ... & Abdullah, A. M. (2021). Electrospun highly corrosion-resistant polystyrene–nickel oxide superhydrophobic nanocomposite coating. Journal of Applied Electrochemistry, 51(11), 1605-1618.‏
الرقم المعياري الدولي للكتاب0021891X
معرّف المصادر الموحدhttps://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=85112638265&origin=inward
معرّف المصادر الموحدhttp://hdl.handle.net/10576/34374
الملخصA key challenge in producing superhydrophobic coatings (SHC) is to tailor the surface morphology on the micro-nanometer scale. In this work, a feasible and straightforward route was employed to manufacture polystyrene/nickel oxide (PSN) nanocomposite superhydrophobic coatings on aluminum alloys to mitigate their corrosion in a saline environment. Different techniques were employed to explore the influence of the addition of NiO nanoparticles to the as-prepared coatings. PSN-2 composite with ~ 4.3 wt% of NiO exhibited the highest water contact angle (WCA) of 155° ± 2 and contact angle hysteresis (CAH) of 5°. Graphic abstract: EIS Nyquist plots of 3 g of electrospun polystyrene coatings (a) without and with (b) 0.1, (c) 0.15, and (d) 0.2 g of NiO. [Figure not available: see fulltext.]
اللغةen
الناشرSpringer Science and Business Media B.V.
الموضوعCorrosion
Nanocomposite
Nickel oxide
Polystyrene
Superhydrophobic
Wettability
العنوانElectrospun highly corrosion-resistant polystyrene–nickel oxide superhydrophobic nanocomposite coating