Corrosion behavior of API-X120 carbon steel alloy in a GTL F-T process water environment at low COD concentration
التاريخ
2020المؤلف
Ewis, DinaTalkhan, Ahmed Gomaa G.
Benamor, Abdelbaki
Qiblawey, Hazim
Nasser, Mustafa
Ba-Abbad, Muneer M. M.
El-Naas, Muftah
...show more authors ...show less authors
البيانات الوصفية
عرض كامل للتسجيلةالملخص
The effect of temperature, time and rotation speed of FT-GTL process water on the corrosion rate of API X-120 carbon steel was investigated. Electrochemical impedance spectroscopy and potentiodynamic polarization techniques were used to determine the carbon steel corrosion rate under temperatures ranging from 293 to 323 K and rotation speed of 0, 500, 1000, 2000 rpm when the immersion time was 0.5, 1, and 2 h. The corrosion rate increased with temperature and rotation speed but decreased with immersion time. SEM, XRD, and XPS analyses of the corroded surfaces confirmed the formation of iron oxide and ferric oxide as the main components of the protective layer.
المجموعات
- الهندسة الكيميائية [1141 items ]
- الأبحاث [494 items ]