Improved mechanical properties of recycled linear low-density polyethylene composites filled with date palm wood powder
Author | AlMaadeed, Mariam A. |
Author | Nógellová, Zuzana |
Author | Janigová, Ivica |
Author | Krupa, Igor |
Available date | 2016-10-02T09:24:12Z |
Publication Date | 2014-06 |
Publication Name | Materials & Design |
Identifier | http://dx.doi.org/10.1016/j.matdes.2014.01.051 |
Citation | Mariam A. AlMaadeed, Zuzana Nógellová, Ivica Janigová, Igor Krupa, Improved mechanical properties of recycled linear low-density polyethylene composites filled with date palm wood powder, Materials & Design, Volume 58, June 2014, Pages 209-216, |
ISSN | 02613069 |
Abstract | Recycled linear low-density polyethylene (RLLDPE) was blended with date palm wood powder to prepare composites in which the concentration of the filler ranged from 10 to 70wt.%. The cross-linking of composites was performed in some selected cases. The Young’s modulus of the composites significantly increased as the filler content increased over the entire concentration range. A maximum value of 1989MPa was observed for the composite filled with 70wt.% filler, which was approximately 6.5times higher than that observed for neat RLLDPE. The presence of filler increased the flexural strength from 11.4MPa for unmodified RLLDPE to 17MPa for the composite containing 70wt.% filler. The Young’s modulus and stress at break measured at 50°C decreased significantly compared with those values measured at 25°C. The ratio between the stress at break at 25°C versus 50°C (σ25/σ50) was between 2.7 and 3.8, whereas the ratio of Young’s modulus of E25/E50 was between 1.6 and 2.6. |
Sponsor | QSTP Grant No. (EXQUQSTP 0906) awarded to Qatar University and also the Scientific Grant Agency of the Ministry of Education of Slovak Republic and the Slovak Academy of Sciences (Project No. 2/0119/12). |
Language | en |
Publisher | Elsevier, Ltd |
Subject | Recycled linear low density polyethylene Date palm wood Composites Mechanical properties Cross-linking Water uptake |
Type | Article |
Pagination | 209-216 |
Volume Number | 58 |
Check access options
Files in this item
Files | Size | Format | View |
---|---|---|---|
There are no files associated with this item. |
This item appears in the following Collection(s)
-
Center for Advanced Materials Research [1349 items ]