عرض بسيط للتسجيلة

المؤلفMusharavati, F.
المؤلفEltai, E. O.
تاريخ الإتاحة2024-02-22T06:33:52Z
تاريخ النشر2020-01-01
اسم المنشورMaterials Today: Proceedings
المعرّفhttp://dx.doi.org/10.1016/j.matpr.2020.07.250
الاقتباسMusharavati, F., & Eltai, E. O. (2021). Permeation of different cations through cathodically protected coated API X-120 steel at elevated temperature. Materials Today: Proceedings, 46, 1600-1607.‏
معرّف المصادر الموحدhttps://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=85112537650&origin=inward
معرّف المصادر الموحدhttp://hdl.handle.net/10576/52078
الملخصThe electrochemical behaviour of coated API X-120 steel in 0.5M of NaCl and KCl with and without cathodic protection (CP) at elevated temperature was investigated. CP was applied at -0.78 and -1.1V vs Saturated Calomel electrode (SCE) on day 5 of immersion. Temperature of solutions was set at 50 °C. Electrochemical Impedance Spectroscopy (EIS) was used to characterize the coating. Energy Dispersive X-Ray Analysis (EDAX) was used to map the metal surfaces. Visual inspection was used to support EIS data. The extent of corrosion was evaluated using Image tool analysis. A correlation was found between the size of the cations and the performance of the coating. Mapping of metal surfaces showed dense areas of Na+ and K+ at -1.1V. K+ was found to be faster than Na+ due to its smaller hydrated size.
اللغةen
الناشرElsevier Ltd
الموضوعCathodic protection
Coated X-120
Corrosion
EIS
Image analysis
Ions permeation
العنوانPermeation of different cations through cathodically protected coated API X-120 steel at elevated temperature
النوعConference Paper
الصفحات1600-1607
رقم المجلد46
dc.accessType Abstract Only


الملفات في هذه التسجيلة

الملفاتالحجمالصيغةالعرض

لا توجد ملفات لها صلة بهذه التسجيلة.

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة