عرض بسيط للتسجيلة

المؤلفAlqaradawi, Siham Y.
المؤلفElnemma, Eman M.
المؤلفKhader, Mahmoud M.
تاريخ الإتاحة2017-02-21T10:54:48Z
تاريخ النشر2004-06
اسم المنشورInternational Journal of Adhesion and Adhesives
المعرّفhttp://dx.doi.org/10.1016/j.ijadhadh.2003.10.001
الاقتباسAlqaradawi, S. Y., Elnemma, E. M. and Khader, M. M.(2004)” Prevention of gallium arsenide photocorrosion by an epoxy adhesion layer” International Journal of Adhesion and Adhesives, vol.24, issue 3, pp. 219–227
الرقم المعياري الدولي للكتاب0143-7496
معرّف المصادر الموحدhttp://www.sciencedirect.com/science/article/pii/S0143749603001283
معرّف المصادر الموحدhttp://hdl.handle.net/10576/5291
الملخصCoating of gallium arsenide with an adhesion layer of commercial epoxy prevented its photocorrosion. A two-component room temperature curing adhesive paste (Araldite 2014) has been selected. When GaAs/Araldite was employed as an anode in a three-electrode photoelectrochemical cell the photogenerated current density decreased significantly due to epoxy coating. However, depositing of few monolayers of Pt on GaAs surface prior to epoxy adhesion increased the photogenerated current density about four times. Moreover, impregnation of the epoxy film with gold enhanced the photogenerated current density significantly. The room temperature electrical conductivity of the epoxy films increased from 10−8 to 10−4Ω−1cm−1 due to gold impregnation. Enhancement of the photocurrent due to gold impregnation is attributed due to better conduction of the photogenerated holes into the electrolyte, also due to activating the adsorption of electrolyte ions.Several parameters are studied with the objective of determining the stability of epoxy films: these are continuous current–voltage (I–E) scans, prolonged illumination, weight changes and surface topography by scanning electron microscopy. All investigations have proven that the epoxy film was quite stable under anodic potentials and illumination in aqueous solutions.
اللغةen
الناشرElsevier Ltd
الموضوعGallium arsenide
Epoxy adhesion
Corrosion prevention
العنوانPrevention of gallium arsenide photocorrosion by an epoxy adhesion layer
النوعArticle
الصفحات219–227
رقم العدد3
رقم المجلد24
dc.accessType Abstract Only