الملخصThe effect of NaNO2 as an inhibitor for corrosion of lead in 0.1 M NaOH solution has been investigated at different temperatures using the Tafel plot technique. The concentrations of NaNO2 employed are in the range 1-5×10-5. There is a linear relationship between the corrosion potential and the molar concentration of NaNO2. The inhibitory effect of Na-NO2 is mainly due to the increase of the polarization resistance of the metal. With rising temperature the polarization resistance decreases considerably and the corrosion rate increases. The maximum inhibition efficiency is found to be 49.4% at 35°C and 45.9% at 50°C.
اللغةen
الناشرCouncil of Scientific and Industrial Research
الموضوعCaustic Soda--Corrosive Effects
Corrosion Protection--Inhibitors
Nitrogen Compounds
Sodium Compounds
Evans Diagram
Inhibitory Effect
Polarization Resistance
Sodium Hydroxide Solution
Sodium Nitrite
Tafel Plot Technique
Lead and Alloys
العنوانInhibitory effect of sodium nitrite on corrosion of lead in 0.1 M sodium hydroxide solution
النوعArticle
الصفحات511-513
رقم العدد10
رقم المجلد26
dc.accessType Abstract Only


الملفات في هذه التسجيلة

الملفاتالحجمالصيغةالعرض

لا توجد ملفات لها صلة بهذه التسجيلة.

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة