Role of the intercalated ions on the high capacitance behavior of Ti 3 C 2 Tx MXene nanohybrids
| المؤلف | Koneru, Bhargavi |
| المؤلف | Swapnalin, Jhilmil |
| المؤلف | Pothu, Ramyakrishna |
| المؤلف | Banerjee, Prasun |
| المؤلف | Boddula, Rajender |
| المؤلف | Radwan, Ahmed Bahgat |
| المؤلف | Al-Qahtani, Noora |
| تاريخ الإتاحة | 2024-09-16T10:35:13Z |
| تاريخ النشر | 2023 |
| اسم المنشور | Nanocomposites |
| المصدر | Scopus |
| الرقم المعياري الدولي للكتاب | 20550332 |
| الملخص | Ti3C2Tx (MXene) is prone to surface oxidation because of the presence of oxygen surface terminals in its surfaces. In this work, the effect of oxygen surface terminals has been reduced by replacing it with other surface terminals or thin layers of heteroatom at the interlayers. These resulted in increasing the interlayer spacing from 9.3 Å up to 12.5 Å with better flexibility properties, thereby facilitating electron/mass transports by exposing enough active surface areas. The carbon nanoplated MXene showed enhanced specific capacitance of 110 F/g at 2 mV/s in LiOH electrolytes for superior supercapacitor applications. |
| راعي المشروع | This work was supported by Qatar University through a National Capacity Building Program Grant (NCBP) [QUCP-CAM-2022-463]. The publication of the article was funded by the Qatar National Library. Statements made herein are solely the responsibility of the authors. Open Access funding was provided by the Qatar National Library. P. Banerjee received financial assistance from SERB, India with grant no TAR/2021/000032. B. Koneru thank SJSGC [F. No. 82-7/2022(SA-III)] UGC JRF research fellowship and J. Swapnalin acknowledge GITAM University for a T. A. fellowship. P. Banerjee acknowledges that the work reported here was supported in part by I-STEM program, funded by the Office of the Principal Scientific Adviser to the Govt. of India. |
| اللغة | en |
| الناشر | Taylor and Francis Ltd. |
| الموضوع | 2D materials intercalated ions MXene nanohybrids nanoplating supercapacitor surface terminations |
| النوع | Article |
| الصفحات | 128-137 |
| رقم العدد | 1 |
| رقم المجلد | 9 |