المؤلفMohamed, Z.
تاريخ الإتاحة2009-11-25T13:03:52Z
تاريخ النشر1992
اسم المنشورEngineering Journal of Qatar University
الاقتباسEngineering Journal of Qatar University, 1992, Vol. 5, Pages 191-199.
معرّف المصادر الموحدhttp://hdl.handle.net/10576/7856
الملخصCorrosion behavior of Ferralium Alloy 255 during service in the environment of concentrated Dead Sea brine has been investigated. It was found that, the corrosion attack is intergranular and exists only in the weld heat effected zone (HAZ). It starts at ferrite/austenite grain boundaries and in the ferrite matrix, where chromium nitride precipitates and then propagates with acceleration in the rest of the metal due to the abrasive action of the slurry.
اللغةen
الناشرQatar University
الموضوعEngineering: Research Teaching
العنوانEvaluation Of Corrosion Resistance Of A Duplex Stainless Steel "Ferralium" In Dead Sea Brine
النوعArticle
الصفحات191-199
رقم المجلد5