Influence Of Surface Finish Parameters On Corrosion Of Zinc

Abstract

The effect of surface parameters on corrosion behaviour of pure zinc in sodium sulphate solution was investigated. Surface parameters were determined using a Talysurf surface analyzer, and corrosion testing was performed using the Tafel plot technique. It was found that the corrosion rate decreases linearly with increasing the grit size while the polarization resistance increases. Also, it was found that the increase in surface roughness has two connecting effects. The first leads to a decrease in corrosion potential due to a decrease in the cathodic surface area while the second leads to an increase in corrosion potential due to a decrease in the peak to valley distances of surface irregularities

تم لى راسة تأثيرطريقة إعداد سمطح العينة على تاكل الزنك النقي في محلول سلفات الصوديوم ، وقد لم قياس معاملات خشونة السطح بواسطة جهاز قياس خشونة الأسطح ( تيليسيرف ) وتم إجراء إختبارات التآكل باستخد ام طريقة ( التافل ) . وقد وجكد أن معدلات التآكل تتناسب تناسبا عكسيا مع زيادة حجم حبيبات التلميع للسطح بينما تقل مقاومة الإستقطاب . وقد أستنتج أن زياده خشونة السطح لها تأثيران متضادان ، أحدهما يؤدي إلى نغص في معدلات التاكل نتيجة نقمى في المساحة الكاثودية بينما يؤدي الآخر إلى زيادة جهد التآكل نتيجة لنقمى المسافات بين المرتفعات والمنخفضات غلى سطح إلعيثات المتآكلة وقد تم التوصل إلى علاقات عددية تربط خشونة السطح مع معدلات التاكل للزنك .