Thermoluminescence induced by gamma radiation In LiCsSO4 Ferroelastic crystal doped With different heavy metals

Abstract

Thermoluminescence (TL) glow curves of lithium cesium sulphate ferroelastic crystals LiCsSO4 doped with 0.5% of Os, Tb, Eu and Tl have been studied in the temperature range from room temperature to 300"C. Three peaks are observed at about 75, 125 and 225"C. The study include also analysis of peak position and peak height of the glow curves with various dopant ions at different gamma radiation doses. The results are interpreted on the basis of point defects introduced interstitially or substitutionally admixtured into the host lattice. In spite of the host material being the swtne (LiCsSO4), the glow curve structure changes due to variation of dopant materials (Os, Tb, Eu, and Tl). The obtained results are discussed in detail. "1 ;e applicability of such materials for accident dosimetry depends on the lower limit of detection.

لقد لمحرست خوامى الوهج الوميضي لبلورات كبريتات الليثيوم والسيزيوم الفيرومرنة والمطعمة بنسبة5ر% من العنامهمر ( Os. Tb, Eu and TI) وكان المدى للحرارة المستخسمة من لمحرجة حرارة الغرفة حتى 300 o م . ولقد لوحظ وجود ثلاثة قسأ ( peaks) - عند لمحرجات حرارة 75 ، 125 ، 225 مْ -ولقد شملت السراسة تحليل منحنيمات الوهج لموضع كل قمة وارتفاعها عند إِختلاف نسب الشوائب داختلاف الجرعات الاشعاعية لأشعة جاما - ولقد فسرت النتائج على أساس النقاط المعيبة الداخلة في الهيجل التنظيمي للبلورات أو التي قد تسث بين الجرئيات في الفراغ البلسي - ولقد وجد أن شكل المنحنيات للوهج الحراسي يتغير باختلاف نوع العنصر المكوق للشوائب المطعحا بها تلك البلورات الفيرومرنة - كما نوقشت النتائج بشيء من التفصيل بالإضافة إلى إمكانيهّ استخدام هذه المواد في الأغرافى السوزيمتوية وخصوصاً في حالة الحوادث الإشعاعية ، حيث يعتمد ذلك على النهالة الصغسى لمدى حساسية تلك المواد للإشعاعات المؤينة .