الملخصIn this paper, the effect of doping of transition metal cations on thermal reduction and CO2 splitting ability of Ce0.9M0.1O2−δ materials (where, M = Ni, Zn, Mn, Fe, Cu, Cr, Co, Zr) is investigated by performing multiple thermochemical cycles using a thermogravimetric analyzer. The Ce0.9M0.1O2−δ materials are successfully derived via co-precipitation method and analyzed via powder X-ray diffraction (PXRD), scanning electron microscope (SEM), and BET surface area analyzer (BET). The Ce0.9M0.1O2−δ materials derived are further tested towards their O2 releasing and CO production capacity by performing ten thermochemical CO2 splitting cycles. The obtained TGA results indicate that CeZn and CeFe are capable of releasing higher amounts of O2 as compared to other Ce0.9M0.1O2−δ materials at 1400 °C. Likewise, these two oxides are again observed to be better than other Ce0.9M0.1O2−δ materials in terms of their CO production capacity at 1000 °C. For instance, CeZn and CeFe releases an average of 50.5 and 50.0 μmol of O2/g·cycle during ten thermochemical cycles in which the thermal reduction step is performed at at 1400 °C. Also, the CO production capacity of CeZn and CeFe material is observed to be equal to 103.3 and 96.3 μmol of CO/g·cycle for ten thermochemical cycles in which the CO2 splitting is carried out at 1000 °C. The compositional and thermal stability of all Ce0.9M0.1O2−δ materials is also analyzed after performing ten thermochemical cycles. The phase composition of all the Ce0.9M0.1O2−δ materials remain unchanged after performing ten thermochemical cycles. However, the crystallite size of all the Ce0.9M0.1O2−δ materials increases after performing the ten thermochemical cycles due to the high temperature processing.
راعي المشروعThis publication was made possible by the NPRP grant ( NPRP8-370-2-154 ) from the Qatar National Research Fund (a member of Qatar Foundation).
اللغةen
الناشرElsevier Ltd
الموضوعCeria
CO
CO2 splitting
Solar fuels
Thermochemical
Transition cations
العنوانTransition metal doped ceria for solar thermochemical fuel production
النوعArticle
الصفحات204 - 211
رقم المجلد172
dc.accessType Abstract Only


الملفات في هذه التسجيلة

الملفاتالحجمالصيغةالعرض

لا توجد ملفات لها صلة بهذه التسجيلة.

هذه التسجيلة تظهر في المجموعات التالية

عرض بسيط للتسجيلة