Performance of corrosion-aged Reinforced Concrete (RC) beams rehabilitated with Fabric-Reinforced Cementitious Matrix (FRCM)
المؤلف | Elghazy, Mohammed |
المؤلف | Refai, Ahmed El |
المؤلف | Ebead, Usama A. |
المؤلف | Nanni, Antonio |
تاريخ الإتاحة | 2021-09-07T06:16:13Z |
تاريخ النشر | 2016 |
اسم المنشور | Sustainable Construction Materials and Technologies |
المصدر | Scopus |
الرقم المعياري الدولي للكتاب | 25153048 |
الملخص | This paper reports on the feasibility of using fabric-reinforced cementitious matrix (FRCM) systems to rehabilitate corrosion-damaged reinforced concrete (RC) beams. Seven large-scale RC beams were constructed and tested to failure under four-point load configuration. Six beams were subjected to an accelerated corrosion process for 70 days to obtain an estimated mass loss of 10% in the tensile steel reinforcing bars. One virgin beam and one corroded unrepaired beam were used as benchmarks for comparison purpose. The other five corroded beams were repaired before applying the FRCM system. The test parameters included the number of fabric plies (1, 2, and 4) and the strengthening schemes (end-anchored bottom flexural strips and fully U-wrapped flexural strips). Test results showed that corrosion insignificantly reduced the yield and the ultimate strength of the specimen. However, the corroded specimen failed to meet the provisions of the ACI 318 code for crack width criteria. The use of FRCM increased the ultimate capacity of corroded beams between 6% and 46% and their yield strength up to 20% in comparison with those of the control virgin beam. The specimens repaired with U-wrapped FRCM strips showed higher capacity and higher ductility than those repaired with the end-anchored bottom strips having similar number of layers. A higher gain in the flexural capacity and a lower ductility index were reported for specimens with higher amount of FRCM layers. 2016 International Committee of the SCMT conferences. All rights reserved. |
راعي المشروع | The project was made possible with the financial support received from Qatar National Research Fund (a member of Qatar Foundation) under NPRP grant # 7-1720-2-641. The statements made herein are solely the responsibility of the authors. |
اللغة | en |
الناشر | International Committee of the SCMT conferences |
الموضوع | Ductility Matrix algebra Reinforced concrete Sustainable development Accelerated corrosion process Cementitious matrices Ductility indices Flexural capacity Reinforced concrete beams Reinforcing bar Ultimate capacity Ultimate strength Steel corrosion |
النوع | Conference Paper |
رقم المجلد | 2016-August |
الملفات في هذه التسجيلة
الملفات | الحجم | الصيغة | العرض |
---|---|---|---|
لا توجد ملفات لها صلة بهذه التسجيلة. |
هذه التسجيلة تظهر في المجموعات التالية
-
الهندسة المدنية [851 items ]