المؤلفHossain, M. I.
المؤلفKhandakar, A.
المؤلفChowdhury, M. E. H.
المؤلفAhmed, S.
المؤلفNauman, M. M.
المؤلفAïssa, B.
تاريخ الإتاحة2023-04-17T06:57:44Z
تاريخ النشر2022
اسم المنشورJournal of Electronic Materials
المصدرScopus
معرّف المصادر الموحدhttp://dx.doi.org/10.1007/s11664-021-09269-w
معرّف المصادر الموحدhttp://hdl.handle.net/10576/41970
الملخصVarious metal oxide thin films, including TiO2, SnO2, MoO3, and NiO, grown by the electron-beam evaporation process, have been optimized for implementation as multilayered structures for infrared (IR) filter-based photonic cooler application. The filter and antireflection coating designs were based on various stacking configurations with titanium dioxide (TiO2) and tin dioxide (SnO2) used as seed layers. These designs were then optimized to achieve wideband optical transmission in the visible spectrum but cut off the infrared region. After deposition, the dual-layer filter configurations were characterized optically and structurally using ultraviolet-visible (UV-Vis) spectrometry, ellipsometry, three-dimensional (3D) profilometry, x-ray diffraction analysis, and scanning electron microscopy. A systematic comparison between these filters confirmed that stacking layers with TiO2 are the best candidate for photovoltaic modules as they demonstrate higher transmission and a clear cutoff after 1000 nm. Finally, computational analysis using OptiLayer software demonstrated a minimum optical reflectance of about 0.4% when coupling an oxide layer with a lower refractive index value (e.g., 1.4) with one having a higher refractive index (> 2). These results illustrate the promising potential of such films for IR filter-based photonic cooling of photovoltaics and/or smart windows. Graphical abstract: [Figure not available: see fulltext.] 2021, The Minerals, Metals & Materials Society.
راعي المشروعThe authors gratefully acknowledge Qatar National Research Fund (QNRF), a member of Qatar Foundation, for funding this work through grant NPRP11S-0117-180330. The authors also thank the QEERI Core Labs team for materials characterization.
اللغةen
الناشرSpringer
الموضوعe-beam evaporation
IR optical filter
Metal oxide
stacking layers
thin films
العنوانNumerical and Experimental Investigation of Infrared Optical Filter Based on Metal Oxide Thin Films for Temperature Mitigation in Photovoltaics
النوعArticle
الصفحات179-189
رقم العدد1
رقم المجلد51
dc.accessType Abstract Only