Optimization of the Consolidation Parameters for Enhanced Thermoelectric Properties of Gr-Bi2Te2.55Se0.45 Nanocomposites

Abstract

Hot pressing represents a promising consolidation technique for ball-milled bismuth telluride alloys, yet deep investigations are needed to understand its effect on the thermoelectric properties. This paper studies the effect of hot-pressing parameters (temperature and pressure) on the thermoelectric properties of the n-type Gr-Bi2Te2.55Se0.45 nanocomposite. Ultra-high pressure, up to 1.5 GPa, is considered for the first time for consolidating Bi2(Te,Se)3 alloys. Results from this study show that increasing the temperature leads to changes in chemical composition and causes noticeable grain growth. On the contrary, increasing pressure mainly causes improvements in densification. Overall, increments in these two parameters improve the ZT values, with the temperature parameter having a higher influence. The highest ZT of 0.69 at 160 °C was obtained for the sample hot-pressed at 350 °C and 1 GPa for 5 min, which is indeed an excellent and competitive value when compared with results reported for this n-type Bi2Te2.55Se0.45 composition.