الملخصThe behaviour of the electrical properties of manganese thin films of different thickness (240 - 1500 A) evaporated under different deposition conditions was studied. The effect of the rate of evaporation (1-7 A/s), the residual gas pressure (10'5 - 10'*' Torr) and the type of residual gas (being air or pure argon) was investigated. Low deposition rates and/or high residual gas pressure resulted in higher resistance values. Using argon instead of air as residual gas enhanced the electrical conductivity.
اللغةen
الناشرQatar University
الموضوعPhysics
الفيزياء
العنوانVariation Of The Electrical Properties Of Manganese Thin Films With Deposition Conditions
العنوان البديلتأثير ظروف التبخير على الخواص الكهربية لأغطية رقيقة من المنجنيز
النوعArticle
الصفحات29-36
رقم المجلد9
الملخص البديليهدف هذا البحث إلى دراسة تأثير ظروف التبخير على الخواص الكهربية لأغشية رقيقة من معدن المنجنيز ذات سمك يتراوح بين 240 - 1500 أنجستروم . تم تحضير تلك الأغشية بطريقة التبخير تحت ضغوط منخفضة تتراوح قيمتها بين 10-5 - 10-6 مم زئبق حيث كان الوسط المحيط بالعينة عند التحضير إما هواء أو معبأ بغاز الأرجون ( الخامل ) . كما تم ترسيب تلك الأغشية على سطوح زجاجية بمعدلات تبخير مختلفة تتراوح ما بين 1 إلى 7 أنجستروم/ث . ولقد بينت الدراسة أن المقاومة الكهربية لأغشية المنجنيز تقل مع زيادة معدل التبخير ومع تناقص الضغط الذي تم تحضيرها عنده . كما أن التبخير في وسط الأرجون يؤدي إلى انخفاض في قيمة مقاومة الغشاء بالإضافة إلى تحسين خواص الغشاء بصفة عامة .