Structural, dielectric and ferroelectric properties of lead-free Na0.5Bi0.5TiO3 ceramics prepared by spark plasma sintering technique
المؤلف | Mudinepalli, V. R. |
المؤلف | Leng, F. |
المؤلف | Reddy, M. P. |
المؤلف | Lin, W. C. |
المؤلف | Murty, B. S. |
تاريخ الإتاحة | 2021-05-20T04:35:57Z |
تاريخ النشر | 2016 |
اسم المنشور | Indian Journal of Physics |
المصدر | Scopus |
الرقم المعياري الدولي للكتاب | 9731458 |
الملخص | Lead-free Na0.5Bi0.5TiO3 (NBT) fine-grained ceramics were prepared by spark plasma sintering method. Single phase ceramics with an ABO3 perovskite structure were confirmed by X-ray diffraction method. The grain morphology was analyzed by using a scanning electron micrograph. The crystal particles arranged compactly and the typical grain size was about ≈200 nm. The depolarization temperature T d, the rhombohedral–tetragonal phase transition temperature T R−T and the temperature T m of the maximum dielectric constant corresponding to tetragonal–cubic phase transition were determined to be 453 K, approximately 623 and 793 K, respectively, from the temperature dependence of dielectric properties. The P-E hysteresis loop at different temperatures indicated the existence of antiferroelectric state at the depolarization temperature T d, which explained the antiferroelectric phase above T d. The values of P s, P r and E c reduced slightly with increasing temperature in the range 303–453 K. |
اللغة | en |
الناشر | Scientific Publishers |
الموضوع | Ceramics Dielectric properties Electrical properties Ferroelectricity X-ray diffraction |
النوع | Article |
الصفحات | 131-138 |
رقم العدد | 2 |
رقم المجلد | 90 |
الملفات في هذه التسجيلة
الملفات | الحجم | الصيغة | العرض |
---|---|---|---|
لا توجد ملفات لها صلة بهذه التسجيلة. |
هذه التسجيلة تظهر في المجموعات التالية
-
الأبحاث [1356 items ]